Sika® Injection-101 RC

Polyurethane flexible injection resin for temporary waterstopping

Sika® Injection-101 RC is a 2-part, polyurethane, low viscous, fast foaming, water-reactive injection resin. It cures to a dense flexible foam.

  • Foaming reaction only takes place in direct contact with water
  • Can be injected as a single component system
  • Free foaming expansion up to 40 times
  • Can be accelerated using Sika® Injection-AC10 in cold temperatures (< + 10 °C)
Product Data Sheet Show all documents

Usage

  • Temporary waterstopping of high water intrusions in cracks, joints and cavities in concrete and masonry.
  • Waterstopping in special applications such as bored or sheet pile walls, anchor heads and microtunneling.
  • To achieve permanent watertight crack sealing inject with Sika® Injection-201 CE or Sika® Injection-203 after temporary waterstopping.
 

Advantages

  • Foaming reaction only takes place in direct contact with water
  • Can be injected as a single component system
  • Free foaming expansion up to 40 times
  • Can be accelerated using Sika® Injection-AC10 in cold temperatures (< + 10 °C)

Packaging

Part A (Resin)10 or 20 kg
Part B ( Hardener)12,5 or 25 kg

Refer to current price list for packaging variations.

Colour

Part A (Resin)Colourless
Part B (Hardener)Brown

Product Details

Sustainability / Certifications / Approvals

SUSTAINABILITY

  • FEICA Environmental Product Declaration (EPD)

APPROVALS / CERTIFICATES

  • Compilation of certified polyurethanes and injection processes for use on structures and components of federal traffic routes ZTV-ING, Part 3, Section 5 (RISS), Sika® Injection-101 RC, Bundesanstalt für Strassenwesen, 20.01.2016

  • Large-surface sealants suitability according to KTW recommendations, Sika® Injection-101 RC, LADR Zentrallabor, July 2019
Product Information

Composition

Water reactive polyurethane resin

Shelf life

24 months from date of production

Storage conditions

The product must be stored in original, unopened and undamaged packaging in dry conditions at temperatures between +5 °C and +35 °C. Always refer to packaging.

Density

Part A (Resin)~1,0 kg/l
Part B (Hardener)~1,25 kg/l

Values at +20 °C

Viscosity

Part A (Resin)

~140 mPa∙s

Part B (Hardener)

~155 mPa∙s

Values at +20 °C
Technical Information

Expansion

Expansion start~15 seconds after contact with water
Expansion end~67 seconds

Values at +20 °C

Application

Application Information

Mixing ratio

Part A : Part B =  1:1 by volume

Reaction times
(PM 10081-11)

0 % Sika® Injection-AC10 *
Material temperature

Expansion start

Expansion end

+5 °C~19 sec~89 sec

+10 °C

~17 sec

~88 sec

+20 °C

~16 sec

~70 sec

5 % Sika® Injection-AC10 *
Material temperatureExpansion start

Expansion end

+5 °C~12 s~57 s
+10 °C~11 s~49 s

+20 °C

~10 s~39 s

10 % Sika® Injection-AC10 *

Material temperature

Expansion start

Expansion end

+5 °C~9 s~41 s

+10 °C

~8 s

~37 s

+20 °C

~7 s

~35 s

* Dosage of Sika® Injection-AC10 in % by weight of Sika® Injection-101 RC (Parts A+B)

 The data above are laboratory parameters and may deviate depending on the situation and conditions on site.

The reaction speed (foam formation) is influenced by the temperatures of the mixed material, the structure and the contact water, plus the hydrodynamic conditions.

Smaller volumes can be used at a ratio of  Part A : Part B =  1:1 by volume

Ambient air temperature

+5 °C min. / +35 °C max.

Substrate temperature

+5 °C min. / +35 °C max.

Pot Life

~2 hours (at + 20 °C)

(ISO 9514)
Application steps

MIXING

Empty Parts A +B into a mixing vessel and mix slowly and thoroughly for at least 3 min (max. 250 rpm) until completely mixed. 

After mixing, pour the material into the pump’s feed container, stir briefly and use within the pot life.

If the substrate and/or ambient temperatures are < +10 °C, Sika® Injection-AC10 can be added to Sika® Injection-101 RC to accelerate the start of expansion.

CLEANING OF EQUIPMENT

Clean all tools and application equipment using the Sika®Injection Cleaning System

Documents