SikaTop®-130 Flex KE
SikaTop®-130 Flex KE is a 2 component flexible waterproofing mortar, cement based, with selected aggregates and modified polymers.
- Low modulus of elasticity, thus achieving good flexibility, reducing the risk of cracking and improving the ability to bridge shrinkage cracks and microcracks
- Waterproof and water vapour permeable
- Withstands both positive and negative pressure
- Predosed
- Excellent adhesion on healthy substrates including concrete, cement mortars, stone, bricks, etc.
- High resistance to de-icing salts and freeze-thaw attack
- Stops the progression of carbonation
- Good crack bridging properties
- Approved for contact with drinking water
Usage
It can be used for waterproofing and protection of surfaces where flexibility is required in order to bridge small cracks. Some of the most common places where it can be used are:- Tanks, swimming pools, canals or other elements intended to contain water, whether buried or not
- Interior waterproofing of basements
- External waterproofing of underground walls
- Repair and protection of surfaces exposed to the action of frost and dicing salts: bridges, terraces and roof overhangs, cornices, etc.
- Protection of concrete surfaces in marine environments
- Waterproofing in contact with drinking water
Advantages
- Low modulus of elasticity, thus achieving good flexibility, reducing the risk of cracking and improving the ability to bridge shrinkage cracks and microcracks
- Waterproof and water vapour permeable
- Withstands both positive and negative pressure
- Predosed
- Excellent adhesion on healthy substrates including concrete, cement mortars, stone, bricks, etc.
- High resistance to de-icing salts and freeze-thaw attack
- Stops the progression of carbonation
- Good crack bridging properties
- Approved for contact with drinking water
Packaging
Pre-weighed batch of 20 kg (5 kg of comp. A and 15 kg of comp. B)
Colour
Component A: White liquid
Component B: Grey powder
Product Details
APPROVALS / CERTIFICATES
- Product for protection against penetration, humidity control and increased resistivity for concrete structures according to UNE-EN 1504-2:2004 with CEmarking and Declaration of Performance 01 07 0101002 0 000007 1053, with certificate of factory production control according to the notifier body No. 0099-CPR-B15-0007.
- Product suitable for contact with drinking water, which meets the requirements of global migrations within the limits indicated in the Regulation 10/2011, according to a test carried out in Instituto Tecnológico del Plástico AIMPLAS
- Waterproof product based on cementituous mortar applied under tiling, class CMO2P, according to UNEEN 14891:2017
Composition
Improved cement mortar with synthetic resins
Shelf life
12 months from date of production if stored properly in undamaged and unopened original sealed packaging in dry and cool conditions
Storage conditions
Liquid component must be protected from frost.
Maximum grain size
0.4 mm
Density
Fresh mortar density: ~ 1.70 kg/l (at +25°C)
Capillary absorption
~0,02 kg/m2·h0.5 (EN 1602-3)
Water penetration under pressure
No penetration after 7 days at 1.5 bar (EN 14891 A.7)
* Values obtained with 2 layers of 2mm each one
Permeability to water vapour
Class I (permeable to water vapour): Sd < 5m
Application
Mixing ratio
Predosed batches
A:B = 1:3 (by weight)
Layer thickness
Min. 1 mm / Max. 2 mm
Ambient air temperature
Min +8 °C/ Max. +35 °C
Substrate temperature
Min +8 °C / Max. +35 °C
Consumption
~1.7 kg/m2/mm. Depending on the roughness of the substrate.
SUBSTRATE QUALITY
- The substrate must be sound, clean, free of grease, oil, friable parts, laitance, and have a minimum resistance of 1 N/mm2.
- In case of irregularities in the substrate, it should be first regularized with a suitable mortar such as the SikaMonotop® range.
- Absorbent substrates should be previously dampened until saturation avoiding flooding and beginning to apply SikaTop®-130 Flex KE when the surfaces acquire a matt appearance.
MIXING
Mixing shall be carried out preferably using a low speed (600 rpm) electric mixer. For this purpose, in a wide mouth and bottom container, pour component B (powder) over component A and mix for 2-3 minutes until a homogeneous mass is obtained.
APPLICATION
The application can be done by trowel, brush, long hair roller or by spraying. The projection equipment will be of type Wagner PC 5, Turbosol T6, Putzmeister gun, etc. The SikaTop®-130 Flex KE can be installed with or without reinforcement.
Without reinforcement:
- If a notched trowel is used, with teeth of 3-4 mm, the first layer is applied with the toothed edge and the second with the plain edge, following the direction of the grooves. The second layer of mortar should be applied when the first has hardened sufficiently (4 to 6 hours at 25 °C).
- If a brush, roller or spray is used for the application, apply two coats waiting for the first to harden before applying the second.
- SikaTop®-130 Flex KE will extend as evenly as possible, avoiding accumulating material in corners, cavities or slits where cracks may appear.
With reinforcement:
- SikaTop®-130 Flex KE coatings armed with ArmaTop®-100, an anti-alkaline fiberglass mesh, are capable of absorbing certain movements that may occur in the element on which they are applied, as well as acting as a bridge in the event that the support presents shrinkage cracks.
- The reinforcement must be carefully placed, avoiding any air occlusion due to the formation of folds or bags in the fiberglass mesh. The fiberglass mesh is joined by overlapping with a width between 3 and 5 cm. The amount of SikaTop®-130 Flex KE to be applied must be the necessary amount to cover the entire reinforcement.
CURING TREATMENT
Measures should be taken to prevent the SikaTop®-130 Flex KE from drying out too quickly by using polyethylene sheets, wet sackcloths or Sika® Antisol® E curing agent.
CLEANING OF EQUIPMENT
Clean all the tools and application equipment with water immediately after use. Hardened material can only be removed mechanically.